Does AutoPIPE have any current or planned abilities for evaluating systems operating at or above the creep threshold? Currently it is possible to evaluate these systems, but there is an error that pops up about revised allowable stress values when operating in this range.
Good question> What possibilities are you thinking about? Keep in mind creep (fatigue/rupture) is a time-dependent failure (mode) that cant be modelled through static analysis. Most design codes do not provide very specific rules for evaluation, afaik.
The Euro code EN13480 in AutoPIPE handles materials in the creep range. It contains many ASME materials when you select the source as ASME. There is a recent related post on how to change piping code from ASME to euro and adjusting the material after conversion.
Perhaps a time dependent dynamic calculation. As creep forms in a system the yield strength decreases, so the allowable stress decreases as well. Modeling and analyzing a creep regime system will work fine for the first ~1,000 hours, but after that its irrelevant as the piping has started to change and will not act in the same way.
I have heard other software, such as ANSYS, can perform this calculation. Since AutoPIPE is one of the bigger players, just wondering if there was a plan for this calculation in the future.
Hello All,
I have sent your questions to the CAE development team for further review.
I will send you more information as I receive it.
Thanks for your time
Regards,
Mike Dattilio
Mike, any word on this? if there needs to be any type of dialog, feel free to contact me. I can email you my contact info if needed.
AutoPIPE already handles creep. You just need to use the European EN13480 piping code. You can specify the lifetime in hours in the same screen where you specify the piping code.